Part name
large low carbon steel grinding plate by sand casting Â
Weight
0.5-150MT
Material
Carbon steel, alloy steel, etc
Application
cement machineryÂ
Standard
ASTM, JIS, GOST, DIN, BS, WCB, etc.
Certification
ISO9001:2008
Inspection
Appearance, dimension, chemical composition, mechanical property, NDT(MT, UT, PT, etc.)
Delivery status
Rough machining; finished machining
Advantage
Factory directly sale, oem service, timely delivery
Incorporate a gating system;Â
Remove the pattern;Fill the mold cavity with molten metal;
Allow the metal to cool;
Break away the sand mold and remove the casting.
Heat treatment.
Chemical composition test,UT/MT test,mechanical property test and so on.
Surface treatment and other requirement from customer.
Standard&certificate:ASTM,BS,NF,DIN,JIS and so on;
 ISO 9001:2008;BV,CCS,DNV,NK,RINA,KR and so on.
Product ShowÂ
Weight:from 3 tons to 150 tons per piece
Application:
The products can be widely used in the area of cement mill,rotary kiln,shipbuilding,
metallurgy,mine,sugar mill,powder plant,rail road,engine bed and so on.
We can provide OEM service for cement mill and rotary kiln casting parts,marine steel casting parts,sugar mill machinery parts with carbon steel or low alloy steel.
The casting parts can be supplied as following treatment:
Heat Treatment: Normalized, normalized and tempered,quench and tempered
Machining: Rough machined,semi-finished machined,finished machined
How to Guarantee the quality?
1.The wooden pattern will be checked carefully by QC team.
2.The casting process will be simulated before pouring.
3.QC will inspect the chemical composition after pouring.
4.QC will do a visual inspection before machining.
5.First time UT and MT will be done after rough machining.
6.Mechanical Property test will be done when the test sample is cut down after heat treatment
7.A final UT and MT will be done after finished machining
8.When the customers visit us for final inspection,they will witness the inspection process again or check the quality with their own test equipment.
What about our service?
7*24h service.
In time response with professional foreign trade team and engineer team.
High quality with reasonable price.
In time delivery.
We are 2.5 hours near to Shanghai and welcome customers to visit our company.
Part name
large low carbon steel grinding plate by sand casting Â
Weight
0.5-150MT
Material
Carbon steel, alloy steel, etc
Application
cement machineryÂ
Standard
ASTM, JIS, GOST, DIN, BS, WCB, etc.
Certification
ISO9001:2008
Inspection
Appearance, dimension, chemical composition, mechanical property, NDT(MT, UT, PT, etc.)
Delivery status
Rough machining; finished machining
Advantage
Factory directly sale, oem service, timely delivery
Incorporate a gating system;Â
Remove the pattern;Fill the mold cavity with molten metal;
Allow the metal to cool;
Break away the sand mold and remove the casting.
Heat treatment.
Chemical composition test,UT/MT test,mechanical property test and so on.
Surface treatment and other requirement from customer.
Standard&certificate:ASTM,BS,NF,DIN,JIS and so on;
 ISO 9001:2008;BV,CCS,DNV,NK,RINA,KR and so on.
Product ShowÂ
Weight:from 3 tons to 150 tons per piece
Application:
The products can be widely used in the area of cement mill,rotary kiln,shipbuilding,
metallurgy,mine,sugar mill,powder plant,rail road,engine bed and so on.
We can provide OEM service for cement mill and rotary kiln casting parts,marine steel casting parts,sugar mill machinery parts with carbon steel or low alloy steel.
The casting parts can be supplied as following treatment:
Heat Treatment: Normalized, normalized and tempered,quench and tempered
Machining: Rough machined,semi-finished machined,finished machined
How to Guarantee the quality?
1.The wooden pattern will be checked carefully by QC team.
2.The casting process will be simulated before pouring.
3.QC will inspect the chemical composition after pouring.
4.QC will do a visual inspection before machining.
5.First time UT and MT will be done after rough machining.
6.Mechanical Property test will be done when the test sample is cut down after heat treatment
7.A final UT and MT will be done after finished machining
8.When the customers visit us for final inspection,they will witness the inspection process again or check the quality with their own test equipment.
What about our service?
7*24h service.
In time response with professional foreign trade team and engineer team.
High quality with reasonable price.
In time delivery.
We are 2.5 hours near to Shanghai and welcome customers to visit our company.
Large Low Carbon Bearing Housing for Rotary Kiln
Model NO.: according to drawings
Surface Treatment: Sand Blast
Surface Roughness: Ra6.3
Standard: ASTM
Certification: ISO 9001:2008
Od: Max.9000mm
Test Report: Chemical Composition,Ut,Mt,Mechanical Property
Certificate: En10204/3.1 and 3.2
Delivery Status: Rough Machining or Finished Machining
Transport Package: Wooden Case or Other Sea Worthy Packing
Specification: ZG270-500
Origin: China
HS Code: 73269090
Model NO.: according to drawings
Surface Treatment: Sand Blast
Surface Roughness: Ra6.3
Standard: ASTM
Certification: ISO 9001:2008
Od: Max.9000mm
Test Report: Chemical Composition,Ut,Mt,Mechanical Property
Certificate: En10204/3.1 and 3.2
Delivery Status: Rough Machining or Finished Machining
Transport Package: Wooden Case or Other Sea Worthy Packing
Specification: ZG270-500
Origin: China
HS Code: 73269090